SPECTROCHIMICA ACTA PART A-MOLECULAR AND BIOMOLECULAR SPECTROSCOPY
卷 103, 期 -, 页码 246-254出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.saa.2012.11.030
关键词
Borate glass; Samarium ion; Absorption; Luminescence; Energy transfer; Lifetime
类别
The Sm3+-doped lead barium zinc lithium fluoroborate (LBZLFB) glasses of composition 20PbO + 5BaO + 5ZnO + 10LiF + (60 - x) B2O3 + xSm(2)O(3), (where x = 0.1, 0.5, 1.0, 1.5 and 2.0 mol%) have been prepared by conventional melt quenching technique and their structural and spectroscopic behavior were studied and reported. The amorphous nature of these glass samples was confirmed with XRD studies. The FT-IR and FT-Raman spectra reveal that, the glasses contain BO3, BO4, non-bridging oxygen and strong OH bonds. The bonding parameters and the oscillator strengths were determined from the absorption spectra. These parameters have been used to obtain the Judd-Ofelt intensity parameters. Using these intensity parameters various radiative and laser properties were predicted. The values of J-O intensity parameters suggested an increase in the degree of symmetry of the local ligand field at Sm3+ sites. The decay rates for the (4)G(5/2) level of Sm3+ ions have been measured and are found to be single exponential at lower concentrations (<1.0 mol%) and turn into non-exponential at higher concentrations (>= 1.0 mol%), due to energy transfer through cross-relaxation. From the emission characteristic parameters of (4)G(5/2) level, it is concluded that the LBZLFB glasses could be useful for photonic devices like visible lasers, fluorescent display devices and optical amplifiers, operated in the visible region. (c) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据