SOLID STATE SCIENCES
卷 18, 期 -, 页码 64-70出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.solidstatesciences.2013.01.001
关键词
IT-SOFC; Symmetric electrode; Reduction; Oxygen-vacancy
资金
- Spanish Ministerio de Ciencia e Innovacion (MICINN) [MAT2010-16404]
A polycrystalline oxygen-stoichiometric La2ZnMnO6 double-perovskite oxide has been prepared by soft-chemistry procedures, followed by annealing in air at 800 degrees C. A reduced specimen, with a La2ZnMnO6 -delta composition, has been obtained by topotactical oxygen removal in an H-2/N-2 (5%/95%) flow at 600 degrees C. The structural characterization has been conducted from neutron powder diffraction (NPD) data, very sensitive to the contrast between Zn and Mn and the oxygen stoichiometry. Both perovskites (oxidized and reduced) crystallize in the monoclinic P2(1)/n space group, exhibiting an antisite Zn/Mn disorder of about 15% and 14%, respectively. The partial reduction of Mn4+ to Mn3+ in the reduced phase is accompanied with the occurrence of oxygen vacancies, located at the axial octahedral sites. Thermogravimetric analysis (TGA) substantiates the oxygen stoichiometry and the stability range. Magnetic susceptibility measurements indicate an antiferromagnetic behaviour, confirming the presence of Mn3+ ions in the structure. The magnetic structure of the reduced phase, determined from NPD data at 3 K, shows an antiferromagnetic G-type coupling between Mn at 2c and 2d sites (promoted by the anti-site disorder); the ordered magnetic moment at Mn site is 0.789 mu(B) at 3 K. Both phases display a semiconductor-like behaviour with a maximum conductivity of 0.052 S cm(-1) for the reduced phase at 650 degrees C, due to the occurrence of Mn3+ -Mn4+ mixed valence. Moreover, the measured thermal expansion coefficients perfectly match with the values usually displayed by SOFC electrolytes. The reversibility and versatility of the present compounds as catalysts for oxygen reduction (cathode) or fuel oxidation (anode) were tested in single SOFC cells yielding power density spanning from 120 to 155 W/cm(2) using these perovskites as anode, cathode and symmetric electrodes for SOFC. (C) 2013 Elsevier Masson SAS. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据