SOLID STATE SCIENCES
卷 11, 期 1, 页码 118-128出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.solidstatesciences.2008.05.020
关键词
Mesoporous; Amorphous; Manganese dioxide; L-Lysine; Hierarchical structure
资金
- NSFC [20373029]
- Ministry of Education [NCET-07-0448]
Hierarchically structured mesoporous MnO2 with high surface area was prepared by a facile precursor route. Well-defined morphological manganese oxalate, synthesized by adding L-Lysine via a hydrothermal method, was used as precursor. Mesoporous amorphous MnO2 with high Brunauer-Emmett-Teller (BET) surface area (340 m(2)/g) and mesoporous Mn2O3 composed of nano-crystals (BET surface area 188 m(2)/g) were obtained by selective calcination of the oxalate precursor at 330 degrees C and 400 degrees C, respectively. Thermogravimetric and differential thermal analyses (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N-2-sorption analysis and X-ray photoelectron spectroscopy (XPS) were used to characterize the structure and property of products. Cyclic voltammetry (CV) and charge-discharge measurements were used to preliminarily stud), the electrochemical performance of the products. The range of pH value (about 5.0-7.0) in the synthesis process is apt to prepare the hierarchical structured manganese dioxide. Other types of amino acids were also employed as the crystallization modifiers and different morphologies of manganese dioxides were obtained. (c) 2008 Elsevier Masson SAS. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据