SOLID STATE IONICS
卷 268, 期 -, 页码 110-116出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.ssi.2014.10.004
关键词
Lithium titanium phosphate; Al-doping; Low temperature; Bulk conductivity; Grain boundary conductivity; Impedance analysis
资金
- Beijing ST Project [Z13111000340000]
- NSFC [51325206]
- Chinese Academy of Sciences [XDA09010202]
A series of Li1+xAlxTi2-x(PO4)(3) samples (x = 0-0.4) were prepared by solid state reaction and were characterized. Lattice parameters a and c decrease continuously with increase of Al content. The relative density of the Al-doped samples is about 97%, which is much higher than 75% of the undoped LiTi2(PO4)(3) sample. Detailed ac impedance measurements from - 150 degrees C to 60 degrees C reveal clearly that three electrical response regions with different relaxation time constants coexist in the undoped LiTi2(PO4)(3) sample but only two in all Al-doped samples. The bulk ionic conductivities for the Al-doped samples show no significant variation from x = 0.1 to x = 0.4. Their ionic conductivities are slightly higher than those of the undoped sample. However, this increase is not caused by increasing bulk ionic conductivity through introducing more lithium ions via doping, but it is mainly attributed to a densification effect. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据