期刊
SOLID STATE IONICS
卷 225, 期 -, 页码 131-135出版社
ELSEVIER
DOI: 10.1016/j.ssi.2012.06.015
关键词
SOEC; LSCM/GDC cathode; Polarization resistance; Steam transport; Co-electrolysis
A composite of (La,Sr)(Cr,Mn)O-3/(Gd,Ce)O-2 (LSCM/GDC) was evaluated as a cathode in a high temperature solid oxide electrolysis cell (SOEC) used for steam electrolysis and/or steam-carbon dioxide co-electrolysis. When the steam feed rate was smaller than 30 ml/min, the LSCM/GDC cathode is subject to large diffusion resistance from inadequate steam supply at steam concentration of 3-20%. Sigmoidal shaped I-V curves were thus observed for steam electrolysis, unlike when CO2 was present during reduction where smooth I-V characteristics were observed. With respect to steam-carbon dioxide co-electrolysis, the ISCM/GDC cathode showed lower performance than for CO2 electrolysis, due to insufficient steam content at a feed of 20% H2O-5% H-2/Ar (10 ml/min) and CO2/CO 70/30 (20 ml/min) mixture. Crown Copyright (c) 2012 Published by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据