SOLID STATE IONICS
卷 192, 期 1, 页码 293-297出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.ssi.2010.07.012
关键词
alpha-Fe2O3; Nanoparticles; Microwave synthesis; Lithium battery; Electrochemical property
Ultrafine alpha-Fe2O3 nanoparticles with an extremely narrow distribution were synthesized by microwave heating. Transmission electron microscopy (TEM) images showed that most primary particles have ellipsoid shapes, and the average diameter of the primary particles was less than 10 nm. The electron diffraction pattern and fringes in some particles in TEM images showed that these nanoparticles were single crystals. The BET surface area of the freeze-dried product was 217 m(2)/g. The initial discharge capacity of the alpha-Fe2O3 nanoparticles exceeded 1007 mA/g (cut-off voltage: 0.5 V). This large capacity corresponds to that calculated by assuming the reduction of Fe3+ to Fe-0 The alpha-Fe2O3 nanoparticles also work as a rechargeable electrode material. The charge-discharge test between 4V and 1.5 V gave a good rechargeable capacity of about 150 mAh/g. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据