SOLID STATE IONICS
卷 181, 期 21-22, 页码 964-970出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.ssi.2010.05.040
关键词
Nanocomposite polymer electrolyte; Hydrotalcite; Clay-nanocomposite; Ionic conductivity
资金
- Council of Scientific and Industrial Research, India
- DST, India
We have prepared a new nanocomposite polymer electrolyte using nanoparticles of hydrotalcite, an anionic clay, as the filler. Hydrotalcite has the chemical composition [M(1-x)(2+) M(x)(3+) (OH)(2)](x+) [A(x/n)(n-)center dot mH(2)O] where M(2+) is a divalent cation (e.g. Mg(2+), Ni(2+), Co(2+),etc.) and M(3+) is a trivalent cation (e.g. Al(3+), Fe(3+), Cr(3+), etc.). A(n-) is an anion intercalated between the positively charged double hydroxide layers. The nanoparticles of [Mg(0.67)Al(0.33) (OH)(2)] [(CO(3))(0.17)center dot mH(2)O] were prepared by the co-precipitation method (average particle size as observed by TEM similar to 50 nm) and were doped into poly(ethylene glycol) PEG (m.w.2000) complexed with LiCIO(4). Samples with different wt.% of hydrotalcite were prepared and characterized using XRD, DSC, TGA, impedance spectroscopy and NMR. Ionic conductivity for the pristine sample, similar to 7.3 x 10(-7) S cm(-1), was enhanced to a maximum of = 1.1 x 10(-5) S cm(-1) for 3.6 wt.% nanoparticle doped sample. We propose that the enhancement of ionic conductivity is caused by percolation effects of the high conductivity paths provided by interfaces between the nanoparticles and the polymer electrolyte. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据