Gel-type dye-sensitized solar cells (DSSCs) were fabricated with 5.0 wt% polyvinyidene fluoride-co-hexafluoro propylene (PVDF-HFP) in methoxy propionitrile (MPN) as gel polymer electrolyte (GPE), 1-butyl-3-methylimidazolium iodide (BMII)/iodine (I-2) as redox couple, 4-tertiary butyl pyridine (TBP) and guanidine thiocyanate as additives. The incorporation of alkyl-modified nanomica (AMNM) in the PVDF-HFP gel electrolytes caused the reduction of crystallization of PVDF-HFP, which was confirmed by X-ray diffraction (XRD) analysis. The short-circuit current density (J(SC)) of the cell increased due to the decrease of diffusion resistance, as judged by the electrochemical impedance spectra (EIS) analysis, while the open-circuit voltage (V-OC) remained almost the same. As the loading of AMNM in the PVDF-HFP gel electrolyte was increased to 3.0 wt%, the J(SC) and power conversion efficiency (eta) of the cells increased from 8.3 to 13.6 mA/cm(2) and 3.5% to 5.7%, respectively. However, the J(SC) decreased as the loading of AMNM exceeded 3.0 wt%. At higher AMNM loadings, nanomica acted as a barrier interface between the electrolyte and the dye molecules to hinder electron transfer, and thus reducing the cell's photocurrent density. Furthermore, the DSSCs fabricated by dispersing polymethyl methacrylate (PMMA) microspheres in the TiO2 electrode with the GPE containing 3.0 wt% AMNM improved the eta to 6.70%. The TiO2 films would exhibit larger porosity by blending with PMMA, leading the penetration of GPEs into the porous TiO2 easier, thus improving the contact between the dye-adsorbed TiO2 surfaces and the GPEs, as characterized by EIS. Moreover, the eta of gel-type DSSCs with a 25 mu m thickness of surlyn reached 7.96% as compared with 6.70% for the DSSCs with a 60 mu m surlyn. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据