期刊
SENSORS AND ACTUATORS B-CHEMICAL
卷 193, 期 -, 页码 616-622出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.snb.2013.12.015
关键词
Cu-doped alpha-Fe2O3; Hydrothermal method; Cubes; Gas sensor
资金
- National Nature Science Foundation of China [61074172, 61134010, 61374218, 61327804]
- Program for Chang Jiang Scholars and Innovative Research Team in University [IRT13018]
- National High-Tech Research and Development Program of China (863 Program) [2013AA030902]
Monodisperse and uniform pure and Cu-doped alpha-Fe2O3 cubes with a hierarchical architecture piled up nanoparticles as secondary units were obtained via a low-cost and environmentally friendly hydrothermal route. The structure and morphology of the as-synthesized products were characterized by X-ray diffraction (XRD), field-emission electron microscopy (FESEM), and transmission electron microscopy (TEM). The XRD results indicated that the lattice constants of doped samples were slightly smaller than that of the pure sample due to Cu incorporation. A comparative gas sensing study between the Cu-doped alpha-Fe2O3 and pure alpha-Fe2O3 cubes was performed to demonstrate the superior gas sensing properties of the doped samples. It was found that the sensor based on Cu-doped alpha-Fe2O3 (3.0 wt%) had a response of 19-100 ppm C2H5 OH, which was about three times higher than that of the pure alpha-Fe2O3 nanostructures at the same operating temperature (225 degrees C). (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据