In this work, unloaded WO3 and 0.25-1.0 wt% Pt-loaded WO3 powders were produced by flame spray pyrolysis (FSP) and structurally characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HR-TEM). The BET surface area (SSA(BET)) of the nanoparticles was measured by nitrogen adsorption. Thick WO3 films (30 mu m) on alumina substrates interdigitated with gold electrodes were prepared by spin-coating technique and tested for gas sensing towards H-2, CO, C2H4 and C2H5OH gases at concentrations ranging from 0.01 to 1 vol% in dry air with operating temperatures ranging from 150 to 300 degrees C. The sensing films exhibited excellent H-2 sensing performances with a very high response, short response time and high selectivity towards CO, C2H4 and C2H5OH gases. The response (within seconds) and recovery (within minutes) times were very fast. It was found that 1.0 wt% Pt-loaded WO3 sensing films showed extremely excellent H-2 sensing performances at 150 degrees C with the highest sensor response (S similar to 1.34 x 10(5)) and the highest selectivity compared to the other gases. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据