期刊
SCRIPTA MATERIALIA
卷 63, 期 2, 页码 246-249出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.scriptamat.2010.03.068
关键词
Fe-Ga alloy; Ductility; Texture; Magnetostriction
类别
资金
- National Science Foundation of China [50775015]
1.0 at.% B-doped Fe83Ga17 sheets 0.05 mm thick were successfully prepared. A sheet with cube texture of {0 0 1}< 1 0 0 > was obtained in the rolled sheets. The temperature and deformation rate in the rolling process and the final annealing atmosphere were all controlled precisely. A large magnetostrictive strain (lambda(parallel to)) of up to 170 ppm was achieved in the 0.26 mm thick rolled sheets under 24 MPa compressive stress with an applied magnetic field along the rolling direction. Crown Copyright (C) 2010 Published by Elsevier Ltd. on behalf of Acta Materialia Inc. All rights reserved.