INT INST SCIENCE SINTERING (I I S S)
DOI: 10.2298/SOS1002245J
关键词
Fired-clay brick; Microstructure; Porosity; Phase analysis; Compressive strength; Water absorption
资金
- Universiti Sains Malaysia
This study is focused on the behaviour of fired-clay brick from the area around Beruas (Malaysia) that is known for it brick industries. The firing temperatures were set from 800 degrees C to 1250 degrees C and soaking time was fixed for an hour The effects of firing temperature on the phase changes, microstructure, compressive strength, water absorption and porosity of the bricks were investigated. Test results indicate that the optimum firing temperature was found to be 1200 degrees C. The percentage of porosity significantly reduces from 39.33% to 5 87% when sintered from 1000 degrees C to 1250 degrees C. Bricks pilfered at 1200 degrees C exhibited the highest strength of 89.5 N/mm(2). The effect of firing temperature significantly improved the microstructure in terms of porosity and the quality of physical properties of fired-clay bricks
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据