SCIENCE AND TECHNOLOGY OF WELDING AND JOINING
卷 20, 期 2, 页码 164-171出版社
MANEY PUBLISHING
DOI: 10.1179/1362171814Y.0000000267
关键词
Ti/Al; Hot dip aluminising; Intermetallic compound; Arc welding brazing
The joint of Al 5A06 and aluminised Ti-6Al-4V dissimilar alloys was achieved by means of tungsten inert gas arc welding brazing. The effect of aluminized coating on the spreading behaviour of filler metal on Ti substrate was studied. The spreadability of liquid filler metal on the Ti substrate was enhanced obviously due to the presence of aluminised coating. The interfacial reaction layer was characterised by a uniform lamellar layer of TiAl3 intermetallic, with a thickness of 1 mm. Sound joints with well appearance were obtained, and the optimised tensile strength of the joint reached 216 MPa. The failure initiated from the interfacial layer at the root face and then propagated within the weld seam at the upper part of the joint. Capable welding parameters were broadened by the presence of aluminised coating for dissimilar metal joining of Ti/Al.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据