Joint formation in dissimilar Al alloy/steel and Mg alloy/steel friction stir spot welds

The microstructural features and overlap shear strength properties of friction stir spot welds made between Al 6111 and low carbon steel, and between Mg alloy AM60 and DP600 dual phase steel, are investigated. When Al 6111 is the upper sheet in the dissimilar sandwich, completed spot welds show evidence of intermetallic layer formation and cracking. Increasing tool pin penetration into the lower sheet provided increased mechanical interlocking of the sheets due to clinching. However, increasing penetration also promoted intermetallic formation and cracking in completed welds. However, dissimilar AM60/DP600 steel friction stir spot welds produced with AM60 as the upper sheet in the dissimilar sandwich do not show evidence of intermetallic formation and cracking may be avoided by removing the zinc coating on the DP600 steel before the friction stir spot welding operation.