期刊
RSC ADVANCES
卷 5, 期 66, 页码 53280-53288出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c5ra09157h
关键词
-
资金
- Knowledge Innovation Program of Institute of Metal Research, Chinese Academy of Sciences [Y0N5A111A1]
- Youth Innovation Promotion Association, Chinese Academy of Sciences [Y2N5711171]
- Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry, P. R. China
Hydrous manganite (MnOOH) nanorods were synthesized by a simple precipitation process in ethanol at room temperature, which eliminated high temperature calcination or a hydrothermal process in the creation of most manganese oxide-based adsorbents and resulted in low energy consumption and subsequently low production cost. These MnOOH nanorods had a high specific surface area at similar to 165.9 m(2) g(-1) and their total pore volume was similar to 0.561 cm(3) g(-1), which was beneficial to their arsenic removal performance. These MnOOH nanorods demonstrated a superior As(III) removal performance from an aqueous environment. At near neutral conditions (pH similar to 7), their arsenic adsorption capacity was over 431.2 mg g(-1), which was among the highest reported values in the literature. The superior As(III) removal performance of these MnOOH nanorods relied on the adsorption and subsequent oxidation of As(III) to less mobilized/toxic As(V), and its fixation on their surface to form inner-sphere arsenic surface complexes.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据