Characterization, activity and mechanisms of a visible light driven photocatalyst: Manganese and iron co-modified TiO2 nanoparticles

An attempt was made to prepare Mn,Fe-codoped nanostructured TiO2 photocatalyst for visible light assisted degradation of an azo dye (methylene blue) in aqueous solutions by a sol-gel process. The asprepared nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV-vis diffuse reflectance spectroscopy (DRS) and photoluminescence spectra (PL) techniques. The photocatalytic activity of Mn,Fe-codoped TiO2 catalyst was evaluated by measuring degradation rates of methylene blue (MB) under visible light. The results showed that doping with the manganese and iron ions significantly enhanced the photocatalytic activity for MB degradation under visible light irradiation. This was ascribed to the fact that a small amount of manganese and iron dopants simultaneously increased MB adsorption capacity and separation efficiency of electron-hole pairs. The results of DRS showed that Mn,Fe-codoped TiO2 had significant absorption between 400 and 500 nm, which increased with the increase of manganese ion content. It is found that the stronger the PL intensity, the higher the photocatalytic activity. This could be explained by the points that PL spectra mainly resulted from surface oxygen vacancies and defects during the process of PL, while surface oxygen vacancies and defects could be favorable in capturing the photoinduced electrons during the process of photocatalytic reactions, so that the recombination of photoinduced electrons and holes could be effectively inhibited.