REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES
卷 110, 期 4, 页码 289-296出版社
REVUE DE METALLURGIE
DOI: 10.1051/metal/2013070
关键词
Cu-Fe composite; annealing treatment; mechanical properties; electrical conductivity
资金
- National High Technology Research and Development Program of China [2007AA03Z519]
- National Natural Science Foundation of China [51004038, 50901019]
- Fundamental Research Funds for the Central Universities [N100609004, N100409009]
- 111 Project of China [B07015]
In this paper, the effect of an annealing treatment on the microstructure, mechanical properties and electrical conductivity of a deformed Cu-12.8 wt%Fe composite prepared by the casting/cold working process is investigated. The Fe filaments exhibit the shape characteristic in the as-drawn composite as the annealing temperature is lower than 500 degrees C. When the annealing temperature is above 500 degrees C, the Fe filaments undergo the instability process in terms of boundary splitting, coarsening and breakup gradually. The tensile strength gradually decreases with increasing annealing temperature due to the coarsening of filament spacing. The work hardening for the composite annealed above 600 degrees C is slower than that annealed at a lower temperature. The electrical conductivity reaches a maximum of 60%IACS at a temperature of 450 degrees C for one hour of annealing, and it further increases with increasing annealing time at 450 degrees C to reach a plateau of 68% IACS. The curve between the tensile strength and electrical conductivity under different annealing processes indicates that the optimum annealing temperature for the Cu-Fe composite is 450 degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据