期刊
JOURNAL OF PROSTHODONTICS-IMPLANT ESTHETIC AND RECONSTRUCTIVE DENTISTRY
卷 26, 期 4, 页码 309-314出版社
WILEY
DOI: 10.1111/jopr.12393
关键词
Dental implant; fracture resistance; resin nano ceramic material; lithium disilicate ceramic; feldspathic ceramic; CAD; CAM blocks; chewing simulation
PurposeTo assess the fracture resistance of single-tooth implant-supported crown restorations made with different CAD/CAM blocks. Materials and MethodsThirty-six titanium abutments were put on dental implant analogs (Mis Implant). For each of three test groups (n = 12/group), implant-supported, cement-retained mandibular molar single crowns were produced. Crowns were made of lithium disilicate glass (LD) IPS e.max CAD, feldspathic glass ceramic (FEL) Vita Mark II, and resin nano-ceramic (RNC) Lava Ultimate. The crowns were cemented with self-adhesive resin cement RelyX Unicem 2. After chewingcycling, crowns were tested to failure in a universal testing machine. Fracture values were calculated as initial (F-initial) and maximum fracture (F-max). ResultsThe study groups were ranked, in order of having highest value, (LD > FEL) > RNC for F-initial load value and (LD > RNC) > FEL for F-max load value. This demonstrated that there was no parallel change in the F-initial and F-max values presenting the fracture resistance of specimens. ConclusionsThere was no accordance between the F-initial and F-max values of the LD, RNC, and FEL after chewing simulation with thermocycling resembling 5 years of clinical functional use. LD had the highest fracture resistance during the fracture test. RNC had low fracture resistance; however, it had considerably high fracture resistance during the fracture test. FEL had considerably low fracture resistance values.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据