Anion-exchange membrane; Pore-filling polymerization; Porous polyethylene; IEC; Electrical resistance; MCDI
资金
- Research Base Construction Fund Support Program - Chonbuk National University in 2018
- Radiation Technology R&D program through the National Research Foundation of Korea - Ministry of Science, ICT & Future Planning [2015M2A2A6021066]
Most polymer membranes with a high ion-exchange capacity (IEC) are not dimensionally stable in water because of their excess water uptake, In this study, an anion-exchange membrane was synthesized by performing a porefilling polymerization in a porous polyethylene membrane used as the supporting substrate. The membrane was found to exhibit a high IEC (3.0 meq/g) but a very low water uptake (8%) and low electrical resistance (0.30 Omega.cm(2)). The membrane capacitive deionization (MCDI) cell assembled from components including the fabricated anion-exchange membrane and a commercial cation-exchange membrane (CMX) was found to exhibit a higher salt adsorption capacity and a higher current efficiency than that using a commercial anion-exchange membrane (AMX, IEC = 1.5 meq/g, electrical resistance = 4.8 Omega.cm(2)) and CMX. This improved performance compared to that of the AMX cell is ascribed to the higher IEC of the new membrane and its lower electrical resistance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据