La-doped Li3V2-xLax(PO4)(3) ( x = 0.01, 0.02, and 0.03) cathode materials for lithium ion batteries were synthesized by the microwave-assisted carbothermal reduction method (MW-CTR). The structures and properties of the prepared samples were investigated by X-ray diffraction (XRD) and electrochemical measurements. The results showed that all the three Li3V2-xLx(PO4)(3) samples had the same monoclinic structures and sharper diffraction peaks of the crystal plane compared with those of the undoped Li3V2(PO4)(3). The initial charge/discharge specific capacity, coulomb efficiency, and discharge decay rate of all the three Li3V2-xLax(PO4)(3) samples were superior to those of the undoped Li3V2(PO4)(3) sample, and the Li3V1.98La0.02(PO4)(3) sample exhibited the best features among the three La-doped Li3V2-xLax(PO4)(3) samples. Electrochemical impedance spectroscopy (EIS) demonstrated that the Li3V1.98La0.02(PO4)(3) sample had a lower charge transfer resistance and a higher Li ion diffusion coefficient compared with the undoped Li3V2(PO4)(3) sample.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据