ACTA METALLURGICA SINICA-ENGLISH LETTERS
卷 28, 期 9, 页码 1190-1197出版社
CHINESE ACAD SCIENCES, INST METAL RESEARCH
DOI: 10.1007/s40195-015-0312-y
关键词
Nanocomposite; SnO2-CuO; Gas sensor; H2S
资金
- National Natural Science Foundation of China [51072141]
- scientific research projects of Education Department of Hubei province [D20141503]
- President Foundation of Wuhan Institute of Technology [2014029]
Nanocomposites composed of SnO2 and CuO were prepared by hydrothermal method. The microstructures of obtained SnO2-CuO powders were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and nitrogen adsorption-desorption test. The results show that the nanocomposites exhibited coral-like nanostructure, and the average crystalline size of SnO2 was 12 nm. The specific surface area of the four samples, SnO2-0.2CuO, SnO2-0.5CuO, SnO2-1.0CuO and SnO2-2.0CuO are 72.97, 58.77, 49.72 and 54.95 m(2)/g, respectively. The gas-sensing performance of the four samples to ethanol, formaldehyde and H2S was studied. The sensor of SnO2-0.5CuO exhibited high response to hydrogen sulfide (4173 to 10 ppm H2S, where ppm represent 10(-6)), and low response to ethanol and formaldehyde. The good selectivity exhibited that the SnO2-0.5CuO nanocomposite can be a promising candidate for highly sensitive and selective gas-sensing material to H2S.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据