PROGRESS IN ORGANIC COATINGS
卷 77, 期 2, 页码 369-379出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.porgcoat.2013.10.012
关键词
Hyperbranched polymer; Fatty acid; Hexamethylene diisocyanate; Coating; Corrosion resistance; Mechanical properties
In the present work, hyperbranched urethane alkyd high solid coatings were formulated by mixing hyperbranched alkyd and isocyanate trimer. Initially, a second generation hyperbranched polyol (HBP) was synthesized using dipentaerythritol (DPE) as a core material and 2,2-bis(methylol)propionic acid (BMPA) as a chain extender. This was reacted with varying concentrations of linseed oil fatty acid (LOFA) to make a series of hyperbranched alkyd (HBA) resins. Viscosity and volume solid of the HBA resins were measured. The resins were characterized by Fourier transform infrared (FTIR), and C-13 Nuclear magnetic resonance (C-13 NMR) spectroscopic techniques. The hyperbranched alkyd resins containing varying amount unreacted hydroxyl groups were cured with hexamethylene diisocyanate (HDI) trimer (Desmodur N 3390) depending on their NCO: OH ratio to make hyperbranched urethane alkyd coatings. A series of such coatings were made by mixing HBA/isocyanate trimer (Desmodur N 3390) ratio with respect to the hydroxyl group present on the HBA. The performance of the coated specimens was evaluated by various techniques such as pull-off adhesion strength, tensile strength, abrasion resistance, scratch resistance, flexibility, and impact resistance tests. The weathering properties of the coated specimens were evaluated by UV-Weatherometer. Corrosion resistance of the coated specimens was evaluated by electrochemical impedance spectroscopy (EIS), salt spray, seawater immersion and humidity tests. It was observed that, there exists an optimum coating composition in terms of NCO: OH (HBA: Desmodur N 3390) ratio which showed excellent enhancement in terms of the mechanical, weathering and corrosion resistance properties than remaining coating compositions. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据