PROCEEDINGS OF THE COMBUSTION INSTITUTE
卷 37, 期 1, 页码 1221-1229出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.proci.2018.07.024
关键词
Flame synthesis; Silica nanoparticles; SiO LIF; LIF thermometry; Kinetics modeling
资金
- German Research Foundation, DFG, within FOR 2284 [SCHU 1369/17, WL63/1]
Depending on the chemical nature of precursor species, the flame-based synthesis of silicon dioxide nanoparticles in lean hydrogen/oxygen flames proceeds via different chemical routes, which affects the generated particle characteristics. Modeling the flame chemistry and particle formation therefore can provide valuable understanding of the underlying gas-phase and particle-formation pathways. In the present study we compare experimentally obtained temperature and semi-quantified SiO-concentration profiles in low-pressure (3 kPa), lean (phi < 0.6), inert-gas diluted H-2/O-2/Ar burner-stabilized flat flames doped with 200-4000 ppm hexamethyldisiloxane (HMDSO) or tetramethylsilane (TMS) with results from kinetics modeling. Temperature fields in the flames were determined via multi-line laser-induced fluorescence (LIF) imaging using both added NO and native SiO as target species. Gas-phase silicon monoxide (SiO) was detected via LIF by exciting the rovibrational Q(42) transition in the A(l)Pi-X-1 Sigma(+) (1,0) vibronic band system at 230.998 nm that provides a weak temperature dependence when analyzing relative SiO mole fractions. Semi-quantitative SiO mole-fraction profiles as a function of height-above-burner (HAB) were obtained for all flames from the measured SiO-LIF intensities corrected for variations of the temperature-dependent ground-state population and the collisional quenching using measured temperatures and effective fluorescence lifetimes, respectively. The experimental data were compared with results of appropriate chemical kinetics mechanisms from the literature with suitable modifications to best reproduce measured SiO mole-fraction profiles. Modeling initial cluster formation is important in this study to unravel the observed 'double-peak'-structure of the SiO concentration profiles assumed to originate from resublimed SiO from early-formed SiO2 nanoparticles in the rising temperature gradient during initial particle nucleation, and which may be altered by the availability of oxygen in the precursor species. (C) 2018 The Combustion Institute. Published by Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据