POWDER TECHNOLOGY
卷 217, 期 -, 页码 489-496出版社
ELSEVIER
DOI: 10.1016/j.powtec.2011.11.008
关键词
Sol-gel process; TiOCl2; Sodium silicate; TiO2 sol; Two-step condensation
资金
- Ministry of Education, Science and Technology
- Ministry of Knowledge Economy of the Republic of Korea
Mesoporous titania-silica composite (MTSC) with a large surface area (387 m(2)/g) and large pore volume was synthesized by a two step condensation sol-gel method. Transparent TiO2 sot was formed at room temperature through condensation and peptization of titanium oxychloride solution using ammonium hydroxide and aqueous nitric acid respectively. Sodium silicate was used as a silica source to form a composite with the preformed TiO2 sol. The physical properties of the composite were examined by Fourier Transform infrared (FTIR), BET surface area. thermogravimetric analysis (TGA), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The nitrogen physisorption behavior of the synthesized composite was compared to that obtained from grafting and one-pot co-condensation methods using the same precursors in the presence of cetyltrimethylammonium bromide (CTAB). It was found that MTSC synthesized under this method possessed large pore sizes and pore volume but its thermal stability was comparatively low. FTIR spectra showed the formation of a Ti-O-Si bond at 940 cm(-1) suggesting that titania was incorporated in silica to form a composite. The XRD patterns showed that the major phase of the titania had an anatase phase up to 900 degrees C but it transforms into rutile when calcined at 1000 degrees C. Furthermore the EDS studies of the as-synthesized and calcined samples substantiated the formation of titania-silica composites. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据