POWDER TECHNOLOGY
卷 205, 期 1-3, 页码 289-291出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.powtec.2010.08.068
关键词
Ceramics; Semiconductors; Nanocrystals; Molten salt synthesis
A molten salt method was proposed to synthesize SrTiO3 nanocrystals in the eutectic NaCl-KCl at 700 degrees C for 6 h, by using the homemade TiO2 nanocrystals and commercial Sr(NO3)(2) powder as raw materials. Besides, a control experiment with the commercial TiO2 submicron-sized crystallites as a precursor was also conducted. The structure and composition of the obtained products were characterized by powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). The results from XRD and XPS revealed the preparation of pure cubic phase SrTiO3 powders. The TEM observation demonstrated that the nanocrystalline TiO2 precursor played an important role in the current molten salt synthesis of SrTiO3 nanocrystals, which were likely formed by the template formation mechanism. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据