期刊
POWDER TECHNOLOGY
卷 201, 期 3, 页码 277-282出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.powtec.2010.04.013
关键词
Dolomite; Thermal treatment; X-ray powder diffraction; SEM; Adsorption
Dolomite powder from Ouled Mimoun, Tlemcen (western region of Algeria) was thermally treated within the temperature range 450-1000 degrees C. The modifications undergone by dolomite, inherent to thermal treatment, were investigated from X-ray diffraction patterns. The results were also discussed using scanning electronic microscopy and nitrogen adsorption. The XRD data, analysed from X Pert Plus program, showed that the dolomite phase ceases at 700 degrees C and is relayed by the formation of in situ calcite and periclase. The crystallographic parameters of these two phases tend towards that of pure periclase and calcite at 1000 and 900 degrees C, respectively. SEM analysis indicated that the morphological properties were profoundly affected. SEM images of D-1000 (sample treated at 1000 degrees C) indicated that the original particle shape of dolomite (presence of discrete grains having sharp edges with presence of cleavages) was totally destroyed, leading to small spherical particles with a diameter of 0.1 mu m. The specific surface area value of D-1000 increased more than 6 times against that of the raw dolomite. Adsorption of azo-dye Orange 1 from aqueous solutions onto untreated and treated dolomites was also reported. The isotherms were of L-type. The interaction was explained by electrostatic considerations between sulfonate groups of the dye (D-SO3Na), which are dissociated in the aqueous system, and positively charged adsorption sites. The affinity of orange I for the dolomitic solids follows the sequence D-900 > D-1000 > D-800 >> D-600 > raw dolomite. The maximum retention capacity shown by D-900 was explained and correlated with its crystallographic properties. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据