Synthesis and properties of a novel double network nanocomposite hydrogel

A novel polyacrylamide/polyacrylic acid (PAAm/PAA) double network (DN) nanocomposite (NC) hydrogel had been synthesized by two-step solution polymerization. The PAAm network was crosslinked by inorganic clay while the PAA network was crosslinked by a chemical crosslinker. The chemical structure of the network was confirmed by Fourier transform infrared (FTIR), X-ray diffraction (XRD), and transmission electron microscopy (TEM). The swelling and mechanical strength properties of PAAm/PAA hydrogels were examined. The results showed that a DN hydrogel achieved both a high swelling capacity of 1219 g/g in deionized water and 124 g/g in 0.9 wt% NaCl solution and high compressive stress of 21.5 kPa in a high water content of 99.58%. Copyright (C) 2008 John Wiley & Sons, Ltd.