POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING
卷 51, 期 12, 页码 1251-1257出版社
TAYLOR & FRANCIS INC
DOI: 10.1080/03602559.2012.699131
关键词
Barrier properties; Low density polyethylene; Montmorillonite; Nanocomposite
资金
- National Foundation of China [51073128]
Montmorillonite (MMT) was first modified with dodecyl dimethylbenzyl ammonium (DDA) salt and octadecyl trimethyl ammonium (OTA) salt. Then low density polyethylene (LDPE)/organic montmorillonite (OMMT) nanocomposites were prepared by twin-screw extruder and hot-press. Transmission electron microscopy (TEM) results showed that OMMT layers were homogeneously intercalated into the LDPE matrix. In terms of MMT, the modification effect of OTA is superior to that of DDA. CO2 and O-2 barrier properties of nanocomposites were increased by 7 times and 4 times with 0.5 wt.% OTA-MMT loading, respectively. At 2 wt% OTA-MMT loading, water vapor permeability of LDPE has also decreased about 2.5 times. Compared with pure PE film, 49.5% and 178% improvement of tensile strength of nanocomposites films were obtained by addition of only 4 wt.% DDA-MMT and OTA-MMT, respectively. In addition, with only 0.5 wt.% OMMT loading, the onset degradation temperature of nanocomposites increases by 23 degrees C and 26 degrees C for LDPE/DDA-MMT and LDPE/OTA-MMT, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据