POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING
卷 51, 期 15, 页码 1545-1549出版社
TAYLOR & FRANCIS INC
DOI: 10.1080/03602559.2012.716131
关键词
Epoxy resin; Kinetic parameters; Linoleate; Polyurethanes; Ricinoleate; Thermal stability
资金
- UGC- New Delhi [33-277/2007 SR]
Epoxy resin of bisphenol-C (EBC), its ricinoleate- and linoleate-based polyols have been cured using 525 wt% triethylamine and toluene-2,4-di-isocyanate at 100 degrees and 140 degrees C, respectively. Cured resins are insoluble in common solvents and characterized by IR, DSC and TGA. Amine-cured resin was thermally stable up to about 309-318 degrees C and followed 1.5-order degradation kinetics. Ricinoleate-based polyurethane was thermally stable up to about 215 degrees C and followed 0.43-, 0.75-, and 1.12-order degradation kinetics. Linoleate-based polyurethane was thermally stable up to about 260 degrees C and followed, respectively, 1.9- and 0.93-order degradation kinetics. Kinetic parameters are interpreted in light of resin structure and nature of hardeners used. Amine-cured epoxy resin possesses better thermal properties than those of its polyols-based polyurethanes.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据