Behaviors of Chemically Crosslinked CAAMPS Hydrogels in Uptake of Uranyl Ions from Aqueous Solutions

Uranyl ion adsorption from aqueous solutions has been investigated by chemically crosslinked (C) polyelectrolyte acrylamide/2-acrylamido-2-methyl-1-propanesulfonic acid (CAAMPS) hydrogels. CAAMPS hydrogels with various compositions were prepared from ternary mixtures of acrylamide (A), 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS), and water by free radical polymerization in an aqueous solution using multifunctional crosslinkers such as ethylene glycol dimethacrylate (EGDMA) and 1,4 butanediol dimethacrylate (BDMA). The swelling equilibrium of polyelectrolyte copolymer gels containing of CAAMPS hydrogels has been studied as a function of copolymer composition. Swelling experiments were performed in water at 25C, gravimetrically. The influence of AMPS content in hydrogels was examined. The weight-swelling ratio of CAAMPS hydrogels was increased up to 127.03 (for 300mg AMPS and crosslinked by EGDMA) and 93.32 (for 300mg AMPS and crosslinked by BDMA), while acrylamide hydrogels swelled up to 10.27 (crosslinked by EGDMA) and 10.06 (crosslinked by BDMA). Uranyl ion adsorption from aqueous solutions was studied by batch sorption technique at 25C. The effect of uranyl ion concentration and mass of AMPS on the uranyl ion adsorption were examined. In the experiments of the sorption, L type sorption in the Giles classification system was found. Finally, the amount of sorbed uranyl ion per gram of dry hydrogel (q) was calculated to be 0.6710-3-2.1110-3 mol uranyl ion per gram for CAAMPS hydrogels. Removal effiency of uranyl ions (RE%) was changed range 9.05-29.92%. The values of partition ratio, (Kd) of uranyl ions was calculated to be 0.10-0.43 for CAAMPS hydrogels.