卷 28, 期 6, 页码 612-617出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymertesting.2009.05.003
关键词
Delamination; Fracture; Fractography; Fatigue; Crack
资金
- Spanish Ministry of Science and Technology [MAT2007-60696]
The mode I and mode II interlaminar fracture surfaces of a unidirectional AS4/8552 carbon/epoxy laminate were studied by means of SEM microscopy and numerical analysis in order to correlate the surface appearance with the stress state. SEM micrographs of fractured surfaces showed that the most predominant fractographic features in modes I and II were 'river markings' and 'hackle markings' respectively. Finite Element Analysis (FEA) showed that the principal tensile stress direction near the crack tip was perpendicular to the 'hackle' or 'stacked lamellae' microstructure and at 45 degrees to the fracture plane. As was observed by other authors, these results suggest that matrix microcracking perpendicular to the principal stress direction is the driving mechanism forming the 'hackle marking' microstructure. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据