Characterization of modified styrene-co-2-acrylamido-2-methylpropane sulfonic acid magnetite nanoparticles

期刊

POLYMER SCIENCE SERIES A
卷 55, 期 5, 页码 327-335

出版社

MAIK NAUKA/INTERPERIODICA/SPRINGER
DOI: 10.1134/S0965545X13050064

关键词

-

资金

  1. King Saud University, College of Science Research Center

向作者/读者索取更多资源

This work provides an insight into the effect of incorporating of magnetite nanoparticles on the rheology of fluids. In this respect, polymer-stabilized magnetite nanoparticles were obtained using sodium salt of poly (2-acrylamido-2-methylpropanesulfonate (PAMPS-Na). Monodisperse polymer coated magnetite nanoparticles Fe3O4/poly(styrene-AMPS) copolymer nanoparticles with diameters of 50-300 nm were prepared by radical polymerization in the presence of a ferrofluid coated with PAMPS-Na. The magnetic nanoparticles were easily separated in a magnetic field. The structure of the obtained magnetic nanoparticles was characterized by Fourier transform infrared spectroscopy (FTIR). The morphology and size of the magnetic nanoparticles were determined by transmission electron microscopy (TEM). FTIR and TEM revealed that the Fe3O4 nanoparticles were incorporated into the shells of poly(styrene-AMPS). Aqueous dispersed solutions of a charged hydrophobically modified Fe3O4/poly(styrene-AMPS) copolymer nanoparticles exhibit high viscosities even at low polymer concentrations (0.1 wt %), which is an interesting feature in connection with enhanced oil recovery. Effects of temperature and addition of sodium chloride on the viscosity properties of a semidilute dispersed solution of Fe3O4/poly(styrene-AMPS) copolymer nanoparticles are examined. The results indicated that Fe3O4/poly(styrene-AMPS) copolymer nanoparticles disclose strong interactions between magnetite and coated polymers of both PAMPS-Na and styrene-AMPS copolymers.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.1
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据