期刊
POLYMER INTERNATIONAL
卷 63, 期 4, 页码 616-625出版社
WILEY-BLACKWELL
DOI: 10.1002/pi.4539
关键词
polyphosphonobetaine; calcium sulfate scale; polyelectrolyte; polyaminophosphonate; antiscalant
资金
- King Abdulaziz City for Science and Technology (KACST) through the Science and Technology Unit at King Fahd University of Petroleum and Minerals (KFUPM) [08-WT76-04]
The cationic monomer N,N-diallyl-3-(diethylphosphonato)propylammonium chloride was cyclo-copolymerized with sulfur dioxide in dimethylsulfoxide using azoisobutyronitrile as initiator to afford a cationic polyelectrolyte (CPE) having a (diethylphosphonato)propyl pendent moiety. The CPE on acidic hydrolysis of the diester groups gave pH-responsive polyzwitterionic acid (PZA) which on treatment with one and two equivalents of NaOH gave zwitterionic/anionic polyelectrolyte (ZAPE) and dianionic polyelectrolyte (DAPE), respectively. The solution properties of CPE, PZA, ZAPE and DAPE were investigated in detail using a viscometric technique. For comparison, the solution properties of the polymers were correlated with those of the structurally similar polyzwitterion prepared from copolymerization of the corresponding zwitterionic monomer ethyl-3-(N,N-diallylammonio)propanephosphonate and sulfur dioxide. Evaluation of antiscaling properties using concentrated brine solutions revealed that DAPE at a meagre concentration of 10 ppm is very effective in inhibiting the formation of calcium sulfate scale, and as such can be used effectively as an antiscalant in reverse osmosis plants. (c) 2013 Society of Chemical Industry
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据