期刊
POLYMER ENGINEERING AND SCIENCE
卷 48, 期 12, 页码 2439-2445出版社
WILEY
DOI: 10.1002/pen.21200
关键词
-
资金
- Korea Science and Engineering Foundation (KOSEF) [R11-2005-065]
- Soongsil University Research Fund
Poly(N-isopropylacrylamide) (PNIPA)/silica composite hydrogels were prepared and the effects of the silica incorporation on the swelling and breaking characteristics of the hydrogels were investigated. To improve the dispersive property of silica in the PNIPA matrix via the formation of covalent bonds between the polymer and silica, vinyl groups were introduced in the silica by reacting it with a coupling agent, 3-methacryloxypropyltrimethoxysilane. When unmodified silica was used as filler in the PNIPA-composite hydrogel, the swelling ratio of the composite hydrogel below the critical gel transition temperature (CGTT) increased with increasing silica content. However, when the modified silica was used as the filler, the swelling ratio below CGTT decreased with increasing silica content because of the enhanced distribution and additional crosslinking. Above CGTT, the swelling ratios of the PNIPA/silica hydrogels were similar regardless of the silica modification. The gel breaking stress of the hydrogels increased with increasing silica content, and this enhancement was larger for the modified silica hydrogel. Scanning electron microscopy images showed that the modified silica particles were distributed more evenly in the PNIPA matrix than the unmodified ones were and that the size of cell-like structure of the hydrogel decreased with increasing modified silica content. POLYM. ENG. SCI., 48:2439-2445, 2008. (C) 2008 Society of Plastics Engineers
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据