期刊
POLYMER DEGRADATION AND STABILITY
卷 96, 期 8, 页码 1508-1515出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2011.05.002
关键词
Synthesis; Application; Flame retardancy; Mechanism; Silicon; Phosphorus
资金
- Chinese 973 National Key Scientific Projects [201103606002]
- Foundation for the Key Project in Science and Technology of Guangdong province [20108010800018]
- Department of Education of Guangdong province [cxzd1008]
A novel flame retardant containing silicon and caged bicyclic phosphate groups, tri(2,6,7-trioxa-1-phosphabicyclo[2.2.2]octane-1-oxo-4-hydroxymethyl) phenylsilane (TPPSi) was successfully synthesized. The chemical structure of TPPSi was characterized by FTIR, H-1 NMR and P-31 NMR. The application of TPPSi (25 wt%) as a flame retardant in polyamide 6 (PA6) not only gains satisfied flame retardancy and smoke suppression, but also retains the high toughness and inherent appearance of pure PA6. The influence of TPPSi on the decomposition pathway of PA6 was discussed based on TG-FTIR and FTIR analysis. The interaction between TPPSi and PA6 at high temperature alters the decomposition pathway of PA6 resulting in the formation of the residue containing phosphorus and silicon. The heat and smoke release behaviors at different external heat fluxes were measured by cone calorimeter, and the fire residue was analyzed by SEM-EDX. The condensed phase action resulting from the barrier effect of residue is proposed to be the major flame retardancy mechanism of TPPSi in PA6, with the fuel reduction action as the minor. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据