A monomer, acryloxyethyl phenoxy phosphorodiethyl amidate (AEPPA), was synthesized and characterized using Fourier transform infrared (FTIR), H-1 nuclear magnetic resonance spectroscopy (H-1 NMR) and P-31 NMR. The copolymer with various amounts of styrene (St) was obtained by the free radical bulk polymerization between AEPPA and St, and characterized using H-1 NMR. The thermal properties of the copolymers were investigated with thermogravimetric analysis (TGA) in air and nitrogen atmosphere, and differential scanning calorimetry (DSC). The TGA results in air indicated the copolymers with AEPPA show higher thermal stability than those without AEPPA. However, the TGA results in nitrogen showed that the decomposition temperature decreased and the char residue increased with the increase of AEPPA. The glass transition temperature (T-g) of the copolymers from DSC indicated that a inverse proportion was observed between T-g and the amount of AEPPA incorporated. The flammability of the copolymers was evaluated by microscale combustion calorimeter (MCC). The MCC results showed that AEPPA can decrease the peak heat release rate (PHRR) and the heat release capacity (HRC), and the sample CP10 shows the lowest PHRR and HRC. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据