期刊
POLYMER DEGRADATION AND STABILITY
卷 95, 期 12, 页码 2574-2583出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2010.07.028
关键词
Conducting fabrics; Polypyrrole; Anthraquinone sulfonic acid; X-ray photoelectron spectroscopy; Scanning electrochemical microscopy
资金
- Spanish Ministerio de Ciencia y Tecnologia
- European Union [CTM2007-66570-C02-02]
- Universidad Politecnica de Valencia [PAID-05-08]
- Conselleria d'Educacio (Generalitat Valenciana)
The stability of conducting fabrics of polyester (PES) covered with polypyrrole/anthraquinone sulfonic acid (AQSA) has been tested in different pH solutions (1, 7, 13) and after washing tests. It is important to determine the stability of the counter-ion in the polymer matrix, since its loss causes the decrease of the conducting properties of the fabrics. X-ray photoelectron spectroscopy (XPS) studies were done to quantify the amount of counter-ion in the polymer and to obtain the doping level (N delta+/N). Surface resistivity changes after the different tests were measured by electrochemical impedance spectroscopy (EIS). An increase in the solution pH caused a decrease of the doping level (N delta+/N), the release of part of the counter-ions and an increase in the surface resistivity. Cyclic voltammetry (CV) measurements showed a gradual loss of electroactivity as pH increased. The influence of the scan rate on the characterization of conducting fabrics has been also demonstrated by CV. Lower scan rates produce a more characteristic response than higher ones. Scanning electrochemical microscopy (SECM) measurements showed a loss of electroactivity when the sample was tested in the pH 13 solution, although the material continued being electroactive. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据