期刊
POLYMER DEGRADATION AND STABILITY
卷 95, 期 12, 页码 2603-2610出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2010.07.025
关键词
Phenylthiourea; Azomethine; Solubility; Thermal stability; Wide-angle X-ray diffraction
资金
- Higher Education Commission of Pakistan (HEC) [063-111354-Ps3-068]
A new diamine, 1,4-phenylene bis((E)-1-(4-chloro-3-aminobenzylidene) thiourea) (PCABT), containing phenylthiourea and azomethine groups was prepared from the reduction of dinitro compound, 1,4-phenylene bis((E)-1-(4-chloro-3-nitrobenzylidene)thiourea), PCNBT. The structures of resulting monomers were characterized by elemental analysis. FTIR, H-1 and C-13 NMR techniques. Afterwards, this diamine was reacted with various aromatic dianhydrides (ODPA, BTDA and 6FDA) in glacial acetic acid to afford poly (phenylthiourea azomethine imide)s (PPTAls) with eta(inh) of 1.59-1.66 dL/g, depending on the dianhydride used. The ensuing PPTAls exhibited ample solubility in organic solvents (DMAc, DMF, DMSO and NMP) and were obtained in quantitative yields. Also, all polyimides were amorphous according to wide-angle X-ray determination. GPC measurements of polymers revealed M-w around 69,000-72,000. Moreover, thermogravimetric analyses indicated that PPTAls were fairly stable up to 550 degrees C, and 10% weight loss temperatures were recorded in the range of 563-578 degrees C (N-2 atmosphere). Ultimately, these polyimides own high glass transition temperatures about 281-285 degrees C. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据