POLYMER DEGRADATION AND STABILITY
卷 95, 期 9, 页码 1736-1742出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2010.05.015
关键词
In vitro; In vivo; Degradation; Injectable; Bone repair
资金
- National Natural Science Foundation of China [50772052]
- Doctor Subject Foundation of the Ministry of Education of China [20070003004]
In vitro and in vivo degradation behaviors of an injectable bone regeneration composite (IBRC) which comprised of nano-hydroxyapatite/collagen (nHAC) particles in alginate hydrogel carrier were investigated. In vitro degradation quantitative testing indicated that the alginate had a faster degradation rate in simulated body fluid (SBF) than in deionized water at 37 degrees C. Similarly, IBRC also had a higher degradation rate in SBF than in deionized water at 37 degrees C, which was evaluated by alginate molecular weight measurement, mechanical properties test and degradation kinetics evaluation. But molecular weight of alginate degraded slower in IBRC than that in aqueous solution. In vitro results showed that degradation medium SBF had influence on degradation of alginate molecules. In the in vivo degradation study, surprisingly, there was no obvious decreasing of molecular weight of alginate from 0 to 8 weeks. IBRC degraded mostly after 24 weeks implantation and was replaced by connective tissue. No fibrous capsule and acute inflammatory reaction were found during the observed 24 weeks after IBRC implantation. There is only a mild short-term inflammatory response in rat dorsum muscle. These results indicated that IBRC had a controllable degradability and biocompatibility. Therefore. IBRC may be a promising degradable material for bone repair and bone tissue engineering. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据