POLYMER CHEMISTRY
卷 5, 期 17, 页码 4939-4947出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c4py00234b
关键词
-
资金
- Natural Science Foundation of China [21104022, 21374034]
- Science and Technology Development Plan of Jilin Province [20130522138JH]
Poly(ether ether ketone) bearing benzyl bromide groups (Br-PEEK) was synthesized and a series of crosslinked membranes (Br-PEEK-x%PBI) based on Br-PEEK with polybenzimidazole (PBI) as a macromolecular cross-linker was prepared to improve the dimensional stability and tensile strength without reducing proton conductivity. X-ray photoelectron spectroscopy (XPS) confirmed the success of the cross-linking reaction. After being ammoniated, the quaternary ammonium PEEK membranes were immersed in phosphoric acid and anhydrous phosphoric acid doped membranes were obtained. The phosphoric acid doped membranes without PBI as the cross-linker had excess volume swelling and could not remain integrated. The other cross-linked membranes had good dimensional stabilities. Because PBI could absorb phosphoric acid, the proton conductivities of cross-linked membranes first increased and then decreased with the content of PBI increasing. The highest proton conductivity was 0.081 S cm(-1) at 200 degrees C for the PA-PEEK-20%PBI membrane. The dimensional stabilities, oxidative stabilities and tensile strength of PA-PEEK-x%PBI membranes improved. The PA-PEEK-30%PBI membrane could last for 7.5 h in 3 wt.% H2O2, 4 ppm Fe2+ Fenton solution at 80 degrees C before breaking into pieces. Energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy (SEM) and dynamic mechanical analysis (DMA) were used for detailed research.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据