期刊
ACTA MATERIALIA
卷 83, 期 -, 页码 397-407出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2014.09.048
关键词
Nanoindentation; Hardness; Orientation dependence; EBSD; WC grain
资金
- Slovak Grant Agency for Science [2/0122/12]
- CE SAS CLTP-MREC
- Hungarian Scientific Research Fund (OTKA) [K109021, K109570]
- Agilent Technologies
The orientation dependence of hardness and nanoindentation-induced deformation mechanisms of differently orientated tungsten carbide (WC) grains in WC-Co hardmetal were studied. Electron backscatter diffraction, atomic force microscopy and scanning electron microscopy investigations were performed to determine the grain orientation, and to study the surface morphology and the resulting deformation fields around the indents. The hardness of the differently orientated WC grains showed significant angle dependence from the basal towards the prismatic directions, but there was only a slight change in hardness between the two types of prismatic orientations ((1 0 (1) over tilde 0) and (2 (1) over bar (1) over bar 0)). Sink-in and pile-up effects, together with highly deformed regions and dislocation steps, were revealed around the imprints in the case of basal and prismatic orientations, respectively. A theoretical model is proposed in which the critical force for slip activation is determined as a function of orientation, based on the possible slip systems of WC. The predictions of the present model concerning the measured hardness values and the deformation field around the indents together with the sink-in effect are in good agreement with the experimental results. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据