In situ SEM observation of a lithium deposition and dissolution process in an all-solid-state lithium metal battery using a sulfide-based solid electrolyte (SE) was carried out. We revealed visually that the morphology of lithium deposition varies with the operating current densities. At current densities higher than 1 mA cm(-2), local lithium deposition triggers large cracks, leading to a decrease in the reversibility of lithium deposition and dissolution. On the other hand, at a low current density of 0.01 mA cm(-2), its homogeneous deposition, which enables the reversible deposition and dissolution, hardly brings about the occurrence of unfavorable cracks. These results suggest that homogeneous lithium deposition on the SE and the suppression of the growth of lithium metal along the grain boundaries inside the SE are keys to achieve the repetitive lithium deposition and dissolution reaction without deterioration of the SE.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据