The synthesis of long-term stable polyoxometalate (POM)-stabilized Pt nanoparticles (NPs) is described here. By means of controlled bulk electrolysis, the reduced POM anions, SiW(12)O(40)(4-) (or SiW(12)) and H(2)W(12)O(40)(6) (or H(2)W(12)), respectively, served the dual role of reductant and protecting/stabilizing ligand for the Pt NPs. Transmission electron microscopy (TEM) images confirmed the formation of 3 to 4 nm sized Pt NPs, which coincidently was in the same size range of the commercial Pt black that was used as a reference. Elemental XPS analyses showed W/Pt ratios of 0.12 for the SiW(12)- and 0.18 for the H(2)W(12)-stabilized Pt NPs, but found no evidence of the presence of Cl(-) anion in the samples. Controlled electrochemical (EC), UV-Vis, and IR data provided unambiguous evidence for the structural integrity of the POM anions on the Pt NP surface. CO stripping, methanol oxidation reaction (MOR), and oxygen reduction reaction (ORR) were used to assess their electrocatalytic activities. It was found that both SiW(12)- and H(2)W(12)-stablized Pt NPs showed enhanced activities in MOR and ORR as compared to that of Pt black, with the latter having higher enhancement. These observations clearly demonstrated that the stabilizing POM anions have a profound influence on the electrocatalytic activity of the underlying Pt NPs.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据