PHYSICA STATUS SOLIDI B-BASIC SOLID STATE PHYSICS
卷 251, 期 12, 页码 2607-2612出版社
WILEY-V C H VERLAG GMBH
DOI: 10.1002/pssb.201451228
关键词
NEXAFS; nitrogen doping; N-2 adsorption; porous carbon; thermal stability
资金
- Russian Foundation for Basic Research [13-03-00884-a]
- Russian Federation [SP-715.2012.1]
- bilateral Program Russian-German Laboratory at BESSY
Nitrogen-containing porous carbon has been produced by acetonitrile vapor deposition at 700 and 800 degrees C on the products of thermolysis of calcium tartrate doped by iron. The template was removed by dilute HCl acid treatment, and the samples obtained were comparatively studied using transmission electron microscopy, N-2 adsorption measurements, thermogravimetric analysis (TGA), X-ray photoelectron and near-edge X-ray absorption fine structure spectroscopy. It was found that increase in the synthesis temperature results in an extension of the specific surface area from similar to 640 to similar to 670m(2)/g, enlargement in the average pore size from similar to 9 to similar to 13 nm, and a decrease in the nitrogen content from similar to 4.4 to 2.7 at%. TGA revealed that the samples differ by similar to 80 degrees C in the temperature of nitrogen loss, which was desorbed as the NO species mainly. [GRAPHICS] Scheme of nitrogen-doped porous carbon synthesis. (C) 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据