期刊
PHYSICA B-CONDENSED MATTER
卷 439, 期 -, 页码 153-159出版社
ELSEVIER
DOI: 10.1016/j.physb.2013.11.023
关键词
CaAl2O4:Eu2+; Nd3+; Boric acid; Flux; Luminescence; Long afterglow
Eu2+ doped and Nd3+ co-doped calcium aluminate (CaAl2O4:Eu2+,Nd3+) phosphor was prepared by a urea-nitrate solution combustion method at furnace temperatures as low as 500 degrees C. The produced CaAl2O4:Eu2+,Nd3+ powder was investigated in terms of phase composition, morphology and luminescence by X-Ray diffraction (XRD), Scanning Electron Microscope (SEM), Fourier Transform Infra Red spectroscopy (FTIR) and Photoluminescence (PL) techniques respectively. XRD analysis depicts a dominant monoclinic phase that indicates no change in the crystalline structure of the phosphor with varying concentration of Eu2+ and Nd3+. SEM results show agglomerates with non-uniform shapes and sizes with a number of irregular network structures having lots avoids and pores. The Energy Dispersive X-ray Spectroscopy (EDS) and (FTIR) spectra confirm the expected chemical components of the phosphor. PL measurements indicated one broadband excitation spectra from 200 to 300 nm centered around 240 nm corresponding to the crystal field splitting of the Eu2+ d-orbital and an emission spectrum in the blue region with a maximum on 440 nm. This is a strong indication that there was dominantly one luminescence center, Eu2+ which represents emission from transitions between the 4f(7) ground state and the 4f(6)-5d(1) excited state configuration. High concentrations of Eu2+ and Nd3+ generally reduce both intensify and lifetime of the phosphor powders. The optimized content of Eu2+ is 1 mol% and for Nd3+ is 1 mol% for the obtained phosphors with excellent optical properties. The phosphor also emits visible light at around 587 and 616 nm. Such emissions can be ascribed to the D-5(0)-F-7(1) and D-5(0)-F-7(2) intrinsic transition of Eu3+ respectively. The decay characteristics exhibit a significant rise in initial intensity with increasing Eu2+ doping concentration while the decay time increased with Nd3+ co-doping. The observed afterglow can be ascribed to the generation of suitable traps due to the presence of the Nd3+ ions. (C) 2013 Elsevier By. All rights reserved,
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据