PHYSICA B-CONDENSED MATTER
卷 407, 期 4, 页码 712-718出版社
ELSEVIER
DOI: 10.1016/j.physb.2011.12.007
关键词
ZnO-ZnF2-B2O3 glass system; Cobalt ions; Spectroscopic properties
The glasses of the composition 10ZnO-30ZnF(2)-60B(2)O(3) doped with different concentrations of Co0 were prepared. Differential scanning calorimetric (DSC) studies, optical absorption, photoluminescence and infrared spectra of these glasses have been carried out. DSC studies have indicated that the resistance of the glass against devitrification increases with the increase in the concentration of CoO. Optical absorption spectra have exhibited one octahedral band due to T-4(1g)(F)-> T-2(1g)(H) and two tetrahedral bands due to (4)A(2)(F-4)-> T-4(1)((4)p) (4)A(2)(F-4)-> T-4(1)(F-4) transitions of Co2+ ions at about 525,570 and 1400 nm, respectively. As the concentration of Co0 is increased the tetrahedral bands are observed to grow at the expense of octahedral band. The luminescence spectra have exhibited two emission bands in the spectral regions of 600-700 nm and 800-900 nm due to T-4(1)(P-4)->(4)A(2)(F-4) and T-4(1)(P-4)-> T-4(2)(F-4) tetrahedral transitions of Co2+ ions, respectively. With the increasing content of cobalt ions in the glass matrix, the half width and intensity of these bands are observed to increase. The analysis of the results of these two spectra coupled with IR spectra has indicated that as the concentration of CoO is increased in the glass matrix, the tetrahedral occupancy of cobalt ions dominates over the octahedral occupancy and increase the rigidity of the glass network. (C) 2011 Elsevier BY. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据