期刊
PHYSICA B-CONDENSED MATTER
卷 406, 期 4, 页码 777-780出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.physb.2010.11.079
关键词
Chemical synthesis; Electromagnetic property; Microwave absorption
资金
- State Key Laboratory of Solidification Processing in NWPU [KP200901]
Flake carbonyl iron (CI) particles and amorphous silica were used to fabricate SiO2-coated Cl particles through the Stober process. The as-prepared SiO2-coated Cl particles were annealed at 500 degrees C for 1 h under argon and air atmosphere. The XRD results showed that only a little amount of oxides were formed when the SiO2-coated Cl particles were annealed under the air atmosphere. The magnetic properties of the SiO2-coated Cl particles before and after annealing treatment showed little change, indicating that amorphous silica appears to be very effective in reducing oxidation of the Cl particles. The reflection loss exceeding -10 dB can be obtained in the frequency range of 9.9-14.6 GHz and a minimum value can be reached to -21.5 dB at 12.2 GHz for the annealed SiO2-coated Cl particles with the composite thickness being 1.5 mm. The mechanism of annealing treatment influence on the electromagnetic properties and microwave absorption of the SiO2-coated Cl particles was also discussed. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据