TRIBOLOGY INTERNATIONAL
卷 88, 期 -, 页码 31-39出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.triboint.2015.03.009
关键词
AlTiN coating; High temperature friction and wear; COF; Wear mechanism
资金
- Jiangsu Province Science and Technology Support Program (Industry) [BE2014818]
An cathodic arc ion plating AlTiN coating was prepared on a YT14 hard alloy. The surface-interface morphologies, the compositions of chemical elements and the phases were analyzed with using SEM (scanning electron microscopy), EDS (energy dispersive spectrometry) and XRD (X-ray diffraction), respectively. Additionally, the surface roughness and grain diameter were observed using AFM (atomic force microscopy). The COFs (coefficients of friction) and wear behaviors of the AlTiN coating were investigated using a high temperature tribological machine at high temperatures (700-900 degrees C), which were measured with a XM808P type PID temperature control instrument. The results show that the N content of the coating is fully released at high temperatures, and the mixed oxides of Al2O3 and TiO2 are formed, improving the wear resistance and lubricating effect of the AlTiN coating. The average COF of the AlTiN coating at 700 degrees C, 800 degrees C and 900 degrees C is 0.77, 0.65 and 0.57, respectively, showing good tribological properties, the wear mechanisms are primarily composed of oxidation wear and abrasive wear, accompanied with fatigue and adhesive wear. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据