OXIDATION OF METALS
卷 73, 期 1-2, 页码 233-253出版社
SPRINGER/PLENUM PUBLISHERS
DOI: 10.1007/s11085-009-9177-7
关键词
FeCrAl; Water vapour; Alumina; Oxidation
资金
- Swedish High Temperature Corrosion Centre (HTC)
- National Graduate School in Materials Science (NFSM)
A Rapidly Solidified Powder (RSP) metallurgical FeCrAl alloy, Kanthal APMT, was exposed in dry and humid O-2 for 72 h at 900-1,100 A degrees C. The formed oxide scales were characterized using gravimetry in combination with advanced analysis techniques (SEM, EDX, TEM, XRD, AES and SIMS). The oxide scales were at all exposures composed of two-layered alpha-Al2O3 scales exhibiting a top layer of equiaxed grains and a bottom layer containing elongated grains. A Cr-rich zone, originating in the native oxide present before exposure, separated these two layers. The top alpha-Al2O3 layer is suggested to have formed by transformation of outwardly grown metastable alumina, while the inward-grown bottom alpha-Al2O3 layer had incorporated small Zr-, Hf- and Ti-rich oxide particles present in the alloy matrix. The scale also contained larger Y-rich oxide particles. Furthermore, in the temperature range studied, the presence of water vapour accelerated alloy oxidation somewhat and affected scale morphology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据