OXIDATION OF METALS
卷 69, 期 3-4, 页码 211-231出版社
SPRINGER/PLENUM PUBLISHERS
DOI: 10.1007/s11085-008-9094-1
关键词
ferritic Fe(Al); internal oxidation; nitridation; kinetics
Exposure of undoped Fe(Al) and Fe(Al)+Cr ferritic alloys in laboratory air at 900-1,000 degrees C resulted in significant internal attack after 5,000 h, including oxides and underlying nitrides. In the most severely attacked alloys, kinetics based on mass gain and maximum penetration depth were linear; also, the deepest penetrations were a significant fraction of the specimen thickness, and were thickness-dependent. Little internal attack was observed at 700-800 degrees C where these compositions may be used as coatings. The extent of internal attack did not decrease with increasing Al or Cr content which may indicate that rather than classical internal oxidation this attack is related to the permeation of N through a defective external scale. No internal attack was observed in alloys doped with Y, Zr, Hf or Ti where the substrate-alumina scale interface was flatter.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据